Thread: EEE gone hard
-
21st September 2010, 02:55 PM #1
Novice
- Join Date
- Sep 2000
- Location
- Toowoomba, QLD, Australia
- Posts
- 1
EEE gone hard
G'day all
I have a tub of EEE-Ultrashine that has gone hard. Am wondering if it can be reconstituted for use. Any help would be much appreciated.
Cheers
Keithg
-
21st September 2010, 06:21 PM #2
Put it in a warm spot . . .
Pat
Work is a necessary evil to be avoided. Mark Twain
-
21st September 2010, 06:51 PM #3
Retired
- Join Date
- May 1999
- Location
- Tooradin,Victoria,Australia
- Age
- 74
- Posts
- 2,515
Have you tried giving it a good stir?
You can add a small amount of turps but it does degrade it or a short burst in the microwave might work but it is better to chuck it out and get a new one.
-
21st September 2010, 07:33 PM #4
G'day ! Is that Pure Turpentine or Mineral Turpentine????
Russell (aka Mulgabill)
"It is as it is"
-
21st September 2010, 08:49 PM #5
Depends on what grade of hard you are talking about.
If rock hard throw out.
If still in a stiff paste then a really good stir will help and a couple of drops of shellawax no more and a good stir.Jim Carroll
One Good Turn Deserves Another. CWS, Vicmarc, Robert Sorby, Woodcut, Tormek, Woodfast
Are you a registered member? Why not? click here to register. It's free and only takes 37 seconds!
-
22nd September 2010, 12:34 AM #6
DO NOT ADD SHELLAWAX!
If as already stated it's rock hard and crispy crunchy, throw it out.
If it's very thick and hard to use it can be melted in hot water or in the microwave on high with 10 second bursts till it melts. REMOVE LID, don't get it too hot, just melt it till it's runny then add some mineral turpentine and stir with a dowel or icy-pole stick etc (nothing metal) till cools enough to show a thickening wake behind the stick. If you don't do this then the abrasive will drop out of the mix.
If there's half a tub add about 20 - 25% turps.
Hope this helps
Cheers - Neil
PS Don't get it so hot that it melts the plastic tub it's in or you won't be too popular.
-
22nd September 2010, 06:03 PM #7
The Oracle has spoken! Mineral Turps it is! Thanks for clearing that up for us Neil
Russell (aka Mulgabill)
"It is as it is"
-
22nd September 2010, 06:58 PM #8
DAMHIKT remove the cardboard seal from the lid before you nuke it...
....................................................................
-
22nd September 2010, 10:31 PM #9
Doh!
There's always one isn't there Harry.
Remove the lid before melting or it may be blown off by the expanding air pressure or the jar may be blown apart for the same reason. Yucky mess may ensue. Massive explosion aside, how else are you going to see if it's melting or not.
-
22nd September 2010, 10:52 PM #10
Neil - can the same method (i.e. judicious microwaving) be applied to Trad Wax that has separated out a bit??
-
22nd September 2010, 11:11 PM #11
Yes. But don't do a Harry.
-
22nd September 2010, 11:21 PM #12
Mmmm...scalding hot wax....
I prefer to keep my massive explosions in the shed where they belong (peers into petrol tank using lighter to check fuel level.....)
-
22nd September 2010, 11:32 PM #13
-
23rd September 2010, 08:10 AM #14
If life was a comic book ZZZZZZT...
....................................................................
-
23rd September 2010, 10:46 AM #15
it might look like this:
Box Challenge 2011 - Check out the amazing Boxes!
Twist One - Wooden Hinge/Latch/Catch/Handle
Twist Two - Found Object
Twist Three - Anything Goes
Similar Threads
-
It's Been A Hard Day
By wheelinround in forum JOKESReplies: 0Last Post: 6th July 2009, 03:38 PM